Tungsten Carbide Insert
Material: 100% fresh WC. CO, Tic,TAC
Grade: Economical. Professional, industrial
Size: standard size &customized size available
Surface treatment:Coating
Application: metalworking, non-ferrous metal working
Processing type: turning
Machine type:turning tools
Sample: <0.5kg, standard size available
Tungsten Carbide Insert for metal non-ferrous metal turning
Xinpin offers various dimension Tungsten Carbide Tungsten Carbide
blanks, semi-finished and finished Insert with universal ,
professional grade to profil various turning work
Features of our Tungsten Carbide Insert
- Ecomonical grade for saving cost, professional & Industrial grade
for high performance,long service life
- Big range of sizes and grades, customized dimension is also
welcomed.
- Manufactory first hand price and ISO certified quality
- Smooth surface, easy to welding
Grade Properties for Tungsten Carbide Insert
| ISO Grade | USA Grade | Physical and Chemical Property | Performance & Applications |
| Density | TRS | Hardness |
| g/cm3 | n/mm2 | HRA |
| P20~P30 | C6 C5 | 12.6 | 1950 | 91.5 | A reasonable match of wear resistance and toughness, versatile
grade. Suitable for rough turning, milling, planning, and
deep-drilling of carbon steel, cast steel, manganese steel,
high-tensile steel, and various alloy steel. A ideal material for
deep-drilling guide block. |
|
|
|
|
| P10 | C7 | 11.3 | 1650 | 92 | Higher wear resistance with a certain impact toughness, Suitable
for semi-finishing of medium chip sections, or finishing of small
chip sections of steel, cast steel, alloy steel. |
| P20 | C6 | 11.4 | 1750 | 91.5 | High strength, good impact and shock resistance. Suitable for rough
turning, finish milling of carbon steel, and alloy steel during
continuous cutting, and semi-finishing and finishing turning during
interrupted cutting . |
| P30 | C5 | 12.9 | 2200 | 90.5 | Best strength, high impact and shock resistance among W-Co-Ti
alloys, but comparatively lower wear resistance. Suitable for rough
turning, rough planning, and semi-finish planning of carbon steel,
and alloy steel including forgings, stamped parts, and cast iron
surfaces during intermittent cutting. |
| M20 | _ | 12.9 | 1880 | 91 | Higher wear resistance and strength, resistant to high impact load.
Suitable for roughing and semi-finishing of ordinary steel, and
cast irons as well as refractory steel, high manganese steel, and
high-grade alloy steel, etc |
| K15 | C3 | 14.9 | 1890 | 91.5 | Fine grain WC alloy, wear resistance higher than YG6, strength
close to YG6. Suitable for machining chilled alloy cast irons, and
refractory alloy steel, as well as finishing of ordinary cast
irons. |
| K20 | C2 | 14.9 | 2050 | 90.5 | High wear resistance, better impact and shock resistance. Suitable
for semi-finishing, and finishing of cast irons, non-ferrous metal,
alloys, and non-metallic materials at moderate cutting speed. |
| K30 | C1 | 14.7 | 2520 | 90 | High strength, better impact and shock resistance, but lower wear
resistance and cutting speed. Suitable for roughing of cast irons,
non-ferrous metal, alloys, and non-metallic materials at low speed. |
Standard dimension for Tungsten Carbide Insert, customized dimension drawing is also welcomed